Properties of syndiotactic‐rich poly(vinyl alcohol) thin film in water. III. Contraction and extension of drawn and annealed thin film in water

摘要

AbstractContraction and extension behaviors in water for drawn (four times original length) and annealed (at 60–215°C) thin films of poly(vinyl alcohol) (PVAVTFA) derived from vinyl trifluoroacetate have been examined. At a constant temperature of 25°C, drawn films annealed at 60–190°C contracted after a certain standing time. Length of films annealed at 200°C did not change after standing of 20 min and film annealed at 215°C extended very little. As the temperature was raised, the drawn films annealed at 60–190°C contracted further until a certain temperature and then extended. The drawn film annealed at 200°C first started contraction at 70°C. The drawn film annealed at 215°C extended further very little until 75°C and then contracted very little until 99°C (in boiling water). In standing at 99°C, it contracted very little with standing and resisted without bre