Factors affecting polymerization of 2‐methyl‐5‐vinylpyridine in poly(ethylene terephthalate) fibers using benzoyl peroxide as initiator

摘要

AbstractPolymerization of 2‐methyl‐5‐vinylpyridine (MVP) in the presence of poly(ethylene terephthalate) fibers (PET) using benzoyl peroxide (BP) as initiator caused a substantial increase in the weight of fibers. The mechanism of this polymerization is believed to be grafting by vinyl addition to PET radical formed under the influence of BP. Increasing the BP concentration up to 4.26 × 10−3mole/l. causes a significant enhancement in grafting, while further increase brings about a marked fall in the graft yield. Increasing the MVP concentration up to 10 also improves significantly the graft yield, but the latter, particularly in the later stages of the reaction, shows lower values at higher MVP concentrations. Raising the reaction temperature from 65° to 95°C causes a significant enhancement in the rate of grafting, though the maximum graft yield obtained at 95°C is much lower than at 85°C. Incorporation of Cu2+ion in the polymerization system enhances the graft yield outstandingly. The same holds true for Fe3+and Li ions, but the enhancement is much less than for Cu2+ion. Addition of acetic or oxalic acid to the reaction decreases the magnitude of grafting. The same situation is encountered when a water/solvent mixture is used as reaction medium. Solvents employed were methanol, ethanol, propanol, and butanol. Also studied was the polymerization reaction with respect to homopolymer, total conversion, and graf