AbstractAt lower than the glass transition temperature, the cleavage of the molecular chains of extended vulcanized rubbers will occur. The crosslinking density of vulcanized rubbers, which were placed at room temperature for about 4 hr in nitrogen atmosphere, increased about 17 after extension of 200 at −76°C. This may be due to the recombination of cleft chains, and this can be shown by the Maxwellian type of curves between crosslinking density and forced strain. Considering the decreasing proportion of crosslinking density by the radical acceptors included in the rubbers and the fact that crosslinking density increases because of recombination of cleft chains, this was attributed to the recombination of unstable chains produced by the added mechanical stimul