Carbon black pastes as coatings for improving thermal gap-filling materials

摘要

Carbon black pastes were found to be effective as coatings for improving the performance of thermal gap-filling materials, including flexible graphite, aluminum and copper. The thermal contact conductance across copper mating surfaces was increased by up to 180 percent. A fluidic form of carbon black paste (based on polyethylene glycol) was more effective than a thixotropic form (based on polyol esters). The carbon black pastes were much more effective as coatings than a commercial silver paste. With a carbon black paste coating, aluminum foil (7 mu m thick) was a superior gap-filling material compared to similarly coated flexible graphite (130 mu m thick). However, without a coating, flexible graphite was superior to aluminum. Commercial silicone-based gap-filling materials were inferior to flexible graphite or aluminum (whether coated or not).