Study on PVA hydrogel crosslinked by epichlorohydrin

摘要

AbstractPoly(vinyl alcohol) hydrogel was prepared by using epichlorohydrin as a crosslinking agent. The molecular weight between crosslinks was calculated. The swelling behavior, as well as mechanical properties, of the hydrogels were examined by weighing and tensile testing, respectively. Values of equilibrium water content of more than 95 were reached while Young's modulus and tensile strength of the hydrogels were about 105dyn/cm2. Crystallization was introduced by drying the hydrogels at 90°C. The dried hydrogel samples were used for swelling kinetic study, then reequilibrated with water and subjected again to tensile testing. Due to the formation of microcrystalline domains in the PVA hydrogel network after annealing, hydrogels with greatly enhanced Young's modulus, tensile strength, and elongation at break were obtained and their equilibrium water content values remained still high, i.e., 87 and 93. © 1992 John WileySons, In