机译:Tungsten content and grain boundary misorientation angle effect on crack blunting in nanocrystalline Ni-W alloy
Nanjing Tech Univ, Dept Mech & Power Engn, Nanjing 210009, Jiangsu, Peoples R China;
Crack blunting; Fracture toughness; Dislocations; Grain boundary; Critical penetration stress; Nanomechanics; Modeling; Simulation;