The effect of alcoholic solutions on the thermomechanical properties of immersed poly(lactic acid) films

机译:The effect of alcoholic solutions on the thermomechanical properties of immersed poly(lactic acid) films

获取原文
获取原文并翻译 | 示例

摘要

Abstract The effects of aqueous and deuterium oxide (D2O) solutions of alcohols (methanol, ethanol, 1‐propanol, 2‐propanol, and 1‐butanol) on the thermomechanical properties of poly(lactic acid)—PLA—films were assessed by dynamic mechanical analysis. The glass transition temperature (Tg) of PLA films immersed in 25, 50, 75, and 100 (v/v) alcoholic solutions were compared with the Tg of films immersed in 100 water and D2O. The Tg of PLA films immersed in methanol and ethanol aqueous solutions decreased as the concentration of the alcohol solutions increased. For methanol and ethanol, the Tg decreased by 8.6 and 7.6°C per 25 (v/v) increase in alcohol, respectively. When the PLA films were immersed in propanol aqueous solutions and butanol, the Tg reached the lowest value at 75 (v/v) and 100 (v/v), respectively. Tg of PLA films immersed in 1‐propanol and 2‐propanol decreased by 8.6 and 8.9°C for every 25 increase in propanol before reaching the minimum value, respectively. Aqueous and D2O solutions had similar effects on Tg. Selective studies of crystallinity evolution, ethanol sorption, degree of swelling, and Hansen solubility parameters of PLA were conducted. This work assists in developing PLA films intended for contact with aqueous‐alcoholic solutions.

著录项

获取原文

客服邮箱:kefu@zhangqiaokeyan.com

京公网安备:11010802029741号 ICP备案号:京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有
  • 客服微信

  • 服务号