Investigation of the effect of carbon post- vs pre-coated metallic bipolar plates for PEMFCs - start-up and shut-down

摘要

In this work, the influence of increased potentials during the start-up/shut-down process on metallic bipolar plates (316L) with the coating system Cr/a-C based on graphite-like carbon is investigated. In comparison to commonly applied post-coated bipolar plates, a new low-cost manufacturing process based on pre-coated metal sheets for bipolar plates was evaluated. By developing a vehicle near start-up/shut-down cycle, a relative humidity of 140 and anode residence time of 0.94 s show the greatest damage potential of the cycle variations. After 2000 start-up/shut-down cycles, pre-coated metallic bipolar plates show no increased voltage loss compared to conventional coatings. Nevertheless, the resistances increase for Cr/a-C post- and pre-coating at the H2 outlet. This correlates with an increased surface roughness of the bipolar plate but otherwise only minor surface changes can be observed. The coating variation has no effect on the extent of catalyst coated membrane thinning or increased content of metal ions. (c) 2021 Hydrogen Energy Publications LLC. Published by Elsevier Ltd. All rights reserved.