Attenuation and rheological analysis of magnetic field-induced responsiveness for the magnetorheological elastomer-based composite

摘要

Abstract A novel self-supporting multi-layer magnetorheological elastomer-based (MRE-based) composite with large magnetic field-induced responsiveness has been designed and fabricated. We characterized its morphological properties, evaluated the impact of fabrication conditions on its field-induced responsiveness, investigated attenuation of its field-induced responsiveness under different storage temperatures along with time and analyzed this mechanism from the perspective of rheology. The results showed that the MRE-based composite had homogeneous dispersing of the magnetic fillers and a clear interface between different layers. The field-induced responsiveness of the MRE-based composite could be affected by the fabrication conditions, and it attenuated at different rates when subjected to different storage temperatures along with time; its attenuation period lasted a few days under room temperature while over one month under low temperature (4 °C). The rheological analysis results indicated a long-term cross-linking process over the storage period along with the attenuation of field-induced responsiveness, which might lead to increasing elasticity (indicated by the loss factor tan δ) and rigidity (indicated by the storage modulus G′) of the MRE-based composite along with the storage period. What’s more, emerging feature of Payne effect could be found on MRE-based composite during cyclic shear, which indicated decline of the mechanical properties due to strain-induced inherent friction. On the other hand, the iron fillers in MRE layer could enhance the shear modulus and lead to MR effect (up to 187) for the whole composite, which benefits to the magnetic field-induced responsiveness, due to the relative strengthen of the MRE layer against the assist layer. This work presents a better understanding on the attenuation of the field-induced responsiveness, which is important for the future application of the MRE-based composite.