Intrinsically Microporous Polymer Nanosheets for High-Performance Gas Separation Membranes

摘要

Microporous polymer nanosheets with thicknesses in the range 3-5 nm and with high apparent surface area (Brunauer-Emmett-Teller surface area 940 m~2 g~(-1)) are formed when the effectively bifunctional (tetrafluoro) monomer used in the preparation of the prototypical polymer of intrinsic microporosity PIM-1 is replaced with an effectively tetrafunctional (octafluoro) monomer to give a tightly crosslinked network structure. When employed as a filler in mixed-matrix membranes based on PIM-1, a low loading of 0.5 wt% network-PIM-1 nanosheets gives rise to enhanced CO_2 permeability and CO_2/CH_4 selectivity, compared to pure PIM-1.