Analysis of polyamide and fluoropolymer backsheets: Degradation and insulation failure in field‐aged photovoltaic modules

摘要

Abstract Durability of photovoltaic (PV) modules is of great concern not only from the point of view of cost‐effectiveness but also from the point of view of safety and sustainability. The backsheet of a PV module is one of the most critical parts of the PV module from the point of view of protection and also one of the most important sources of PV modules' failure; hence, it is of great importance to understand its different forms of failure. In this paper we analyze the case of an 8‐MW PV plant, which had suffered a rapid degradation of their PV modules' backsheets. The case is especially relevant as all the PV modules are from the same model and manufacturer but with different backsheet materials (polyamide and fluoropolymer) and different times of exposure: on one hand, all PV modules originally installed in the plant (i.e., 6?years under operation when tested), and also, extra modules that had been stored indoors for replacement and had been mounted in the plant for less than 1?year when tested, serving as reference modules. In this paper we present the signs of degradation of these PV modules after different times of exposure under real operation using different on‐field and laboratory tests. We propose different techniques for rapid diagnosis of backsheet degradation so that the problem can be detected at a very early stage, before it results in major energy losses or in safety issues.