Nonpyrophoric aminophosphines reacted with indium(III) halides in the presence of zinc chloride have emerged as promising phosphorus precursors in the synthesis of colloidal indium phosphide (InP) quantum dots (QDs). Nonetheless, due to the required P/In ratio of 4:1, it remains challenging to prepare large-sized (>5 nm), near-infrared absorbing/emitting InP QDs using this synthetic scheme. Furthermore, the addition of zinc chloride leads to structural disorder and the formation of shallow trap states inducing spectral broadening. To overcome these limitations, we introduce a synthetic approach relying on the use of indium(I) halide, which acts as both the indium source and reducing agent for aminophosphine. The developed zinc-free, single-injection method gives access to tetrahedral InP QDs with an edge length > 10 nm and narrow size distribution. The first excitonic peak is tunable from 450 to 700 nm by changing the indium halide (InI, InBr, InCl). Kinetic studies using phosphorus NMR reveal the coexistence of two reaction pathways, the reduction of transaminated aminophosphine by In(I) and via redox disproportionation. Etching the surface of the obtained InP QDs at room temperature with in situ-generated hydrofluoric acid (HF) leads to strong photoluminescence (PL) emission with a quantum yield approaching 80%. Alternatively, surface passivation of the InP core QDs was achieved by low temperature (140 degrees C) ZnS shelling using the monomolecular precursor zinc diethyldithiocarbamate. The obtained InP/ZnS core/ shell QDs that emit in a range of 507-728 nm exhibit a small Stokes shift (110-120 meV) and a narrow PL line width (112 meV at 728 nm).
展开▼