Residual stress profiling in the ferrite and cementite phases of cold-drawn steel rods by synchrotron X-ray and neutron diffraction

摘要

Residual stress profiles have been measured in the ferrite and cementite phases of a cold-drawn eutectoid steel rod by neutron and synchrotron X-ray diffraction in three orientations (axial, radial and hoop). Neutron diffraction was employed to measure the ferrite stresses, whereas synchrotron radiation was used for ferrite and cementite stresses. Experimental results in the ferrite phase showed excellent agreement between both experimental techniques when gauge volume effects were accounted for. Axial cementite stresses were always tensile, with a maximum value close to 1700 MPa at the rod surface. Radial and hoop cementite stresses were compresive along the diameter of the rod, with a minimum of -1900 MPa at the rod center. A 3D-finite element simulation of the macro residual stresses resulting from cold-drawing showed remarkable agreement with those determined from the experimental measurements in the ferrite and cementite phases.