The partial liquidus projection and solidification sequences in Ti-(40-60) Al-(5-30) Nb alloys

机译:Ti-(40-60)Al-(5-30)Nb合金中的部分液相突出和凝固序列

获取原文
获取原文并翻译 | 示例
   

获取外文期刊封面封底 >>

       

摘要

The properties of Ti-Al-Nb alloys strongly depend on alloy compositions and microstructures. Proper design of these important aspects requires detailed knowledge of the solidification sequences and liquidus projection. However, there are still some conflicts between previous experimental and calculated results about the liquidus projections in the composition range of Ti-(40-60)Al-(5-30)Nb and this has hindered Ti-Al-Nb alloy development. In this present work, we explicitly investigated the as-cast microstructures and phase constitution of 50 alloys with the composition range of Ti-(40-60)Al-(5-30)Nb and clarified the solidification sequences. We re-constructed the partial liquidus projection and found that the primary beta phase region extend to just below 55 at.% Al content and the primary alpha phase region extend to just below 24 at.% Nb content. Moreover, it was observed that the invariant reaction between Liquid, beta, alpha and gamma phases is a peritectic reaction (Liquid+beta+gamma ->alpha) and all the Liquid+beta+gamma, Liquid+beta+alpha and Liquid+alpha+gamma three-phase regions are of peritectic type. The present work provides essential information necessary for optimizing the Ti-Al-Nb thermodynamic database to accelerate alloy development. (C) 2020 Elsevier B.V. All rights reserved.
机译:Ti-Al-Nb合金的性能在很大程度上取决于合金成分和微观结构。正确设计这些重要方面需要对凝固顺序和液相线投影有详细的了解。然而,以往的实验结果与计算结果在Ti-(40-60)Al-(5-30)Nb组成范围内的液相线投影仍存在一定的矛盾,阻碍了Ti-Al-Nb合金的发展。在本研究中,我们明确研究了成分范围为Ti-(40-60)Al-(5-30)Nb的50种合金的铸态组织和相组成,并阐明了凝固顺序。我们重新构造了部分液相线投影,发现初级β相区域延伸到略低于55 at.%铝含量和初级α相区域延伸至略低于24 at.%Nb含量。此外,观察到液体、β、α和γ相之间的不变反应是包晶反应(液体+β+γ->α),所有液体+β+γ、液体+β+α和液体+α+γ三相区域都是包晶型。本工作为优化Ti-Al-Nb热力学数据库以加速合金开发提供了必要的信息。(C) 2020爱思唯尔B.V.版权所有。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱:kefu@zhangqiaokeyan.com

京公网安备:11010802029741号 ICP备案号:京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有
  • 客服微信

  • 服务号