Treatment of Lateral Tibial Condylar Fractures Using Bioactive, Bioresorbable Forged Composites of Raw Particulate Unsintered Hydroxyapatite/Poly-L-Lactide Screws

摘要

Forged composites of raw particulate unsintered hydroxyapatite/poly-L-lactide (F-u-HA/PLLA) devices possess high mechanical strength, bioactivity, and radio-opacity. The aim of this study was to assess the efficacy of F-u-HA/PLLA screws in the treatment of lateral tibial condylar fractures. From January 2005 to December 2010, a total of 7 patients with displaced closed lateral tibial condylar fractures (Schatzker type II) were treated using F-u-HA/PLLA screws. Open reduction and internal fixation was performed using 2 or 3 F-u-HA/PLLA screws. After surgery, weight bearing was not allowed for 6 weeks. Range of motion exercise was initiated after removal of the plaster splint. Radiographs were evaluated for fracture healing, joint depression, and the radio-opacity of F-u-HA/PLLA screws. Clinical outcomes and postoperative complications were also assessed. Average follow-up was 44 months. All fractures were successfully healed. Average values for joint depression were 4.7 mm (range, 2-9 mm) preoperatively, 0.4 mm (range, 0-1 mm) postoperatively, and 0.4 mm (range, 0-1 mm) at final follow-up. Whole shadows of F-u-HA/PLLA screws were observed during the follow-up period. Breakage of screws, osteolysis, and a radiolucent zone around the screws were not observed at final follow-up. Average knee flexion and extension were 134 degrees (range, 110 degrees to 150 degrees) and -1 degrees (range, -10 degrees to 0 degrees), respectively. No patient had wound infection, late aseptic tissue response, or foreign body reaction postoperatively. None of the patients reported pain at final follow-up. These results suggest that F-u-HA/PLLA screws could be an alternative option for the treatment of lateral tibial condylar fractures.