Mechanical properties, morphology, and crystallization behavior of blends of poly(L-lactide) with poly(butylene succinate-co-L-lactate) and poly(butylene succinate)

摘要

The blends of poly(L-lactide) (PLLA) with poly(butylene succinate) (PBS) and poly(butylene succinate-CO-L-lactate) (PBSL) containing the lactate unit of ca. 3 mol% were prepared by melt-mixing and subsequent injection molding, and their mechanical properties, morphology, and crystallization behavior have been compared. Dynamic viscoelasticity and SEM measurements of the blends revealed that the extent of the compatibility of PBSL and PBS with PLLA is almost the same, and that the PBSL and PBS components in the blends with a low content of PBSL or PBS (5-20 wt%) are homogenously dispersed as 0.1-0.4 mu m particles. The tensile strength and modulus of the blends approximately followed the rule of mixtures over the whole composition range except that those of PLLA/PBS 99/1 blend were exceptionally higher than those of pure PLLA. All the blends showed considerably higher elongation at break than pure PLLA, PBSL, and PBS. Differential scanning calorimetric analysis of the blends revealed that the isothermal and non-isothermal crystallization of the PLLA component is promoted by the addition of a small amount of PBSL, while the addition of PBS was much less effective. (c) 2006 Elsevier Ltd. All rights reserved.