Current fractographic research and its application II: environmental fracture (I) --stress corrosion cracking and hydrogen embrittlement

Hitoshi Uchieda; Shigeharu Hinotani

首页> 外文期刊>材料 >Current fractographic research and its application II: environmental fracture (I) --stress corrosion cracking and hydrogen embrittlement

【24h】

Current fractographic research and its application II: environmental fracture (I) --stress corrosion cracking and hydrogen embrittlement

机译：当前的分形研究及其应用二：环境断裂（一）-应力腐蚀开裂和氢脆

获取原文

获取原文并翻译 | 示例

获取外文期刊封面封底 >>

开具论文收录证明 >>

文献代查 >>

页面导航

著录项
相似文献
相关主题

著录项

来源
《材料》 |1998年第7期|共6页
作者
Hitoshi Uchieda; Shigeharu Hinotani;
展开▼
作者单位

展开▼
收录信息
原文格式 PDF
正文语种 jpn
中图分类工程材料学;
关键词
Stress corrosion cracking; Hydrogen embrittlement; Fractography; Crack orientation; Image processing;

机译：应力腐蚀开裂;氢脆;分形;裂纹取向;图像处理;

相似文献

外文文献
中文文献
专利

1. Current fractographic research and its application II: environmental fracture (I) --stress corrosion cracking and hydrogen embrittlement [J] . Hitoshi Uchieda, Shigeharu Hinotani 材料 . 1998,第7期

机译：当前的Fretography Research及其应用II：环境骨折（i） - 斗士腐蚀裂解和氢脆
2. Current fractographic research and its application Ⅲ: environmental fracture Ⅱ -corrosion fatigue- [J] . Ryuichiro Ebara 材料 . 1998,第8期

机译：当前的Fretography Research及其应用Ⅲ：环境骨折Ⅱ-Corrosion疲劳 -
3. Current fractographic research and its application Ⅲ: environmental fracture Ⅱ -corrosion fatigue- [J] . Ryuichiro Ebara 材料 . 1998,第8期

机译：当前的分形研究及其应用Ⅲ：环境断裂Ⅱ-腐蚀疲劳-
4. Current problems with buried pipelines: monitoring cathodic protection, local conditions at coating defects, stray-currents, AC corrosion, stress corrosion cracking, hydrogen stress cracking [C] . A. Pourbaix, Ph. Carpentiers, R. Gregoor International Corrosion Congress . 2002

机译：埋下管道的当前问题：监测阴极保护，涂层缺陷的局部条件，杂散电流，交流腐蚀，应力腐蚀裂纹，氢胁迫开裂
5. Stress corrosion cracking and hydrogen embrittlement of martensitic Alloy EP-823. [D] . Hossain, Mohammad Kamal. 2004

机译：马氏体合金EP-823的应力腐蚀开裂和氢脆。
6. Combined Effect of Alternating Current Interference and Cathodic Protection on Pitting Corrosion and Stress Corrosion Cracking Behavior of X70 Pipeline Steel in Near-Neutral pH Environment [O] . Liwei Wang, Lianjun Cheng, Junru Li, 2018

机译：交流干扰和阴极保护对X70管线钢在近中性pH环境下点蚀和应力腐蚀开裂行为的综合影响
7. Fractographic Study on the Mechanism for Hydrogen Embrittlement Type Stress Corrosion Cracking in Duplex Stainless Steels. [O] . Masato MURATA, Jing-bo WANG, Yoshihiko MUKAI 1991

机译：双相不锈钢氢脆型应力腐蚀机理的特性研究。
8. Stress-Corrosion Cracking of Metallic Materials. Part III. Hydrogen Entry and Embrittlement in Steel. [R] . fontana,mars g. staehle,roger w. 1975

机译：金属材料的应力腐蚀开裂。第三部分。钢中氢的进入和脆化。

Current fractographic research and its application II: environmental fracture (I) --stress corrosion cracking and hydrogen embrittlement

著录项

相似文献

相关主题

期刊订阅