Tribological effect of iron oxide residual on the DLC film surface under seawater and saline solutions

摘要

This paper discusses the seawater and saline solutions effects on the tribological behavior of diamond-like carbon (DLC) films. The adsorption of Fe on DLC surface is one of the mechanisms that is believed to be the cause of the decrease in dispersive component of the surface energy and increase of the I_D/I_G ratio leading to low friction coefficient and wear rate under corrosive environments. Tribological behaviors DLC films were experimentally evaluated under corrosive environments by using steel ball and DLC coated steel flat under rotational sliding conditions. The DLC films were prepared on 440 stainless steel disks by DC-pulsed PECVD using methane as a precursor gas. Two different set of tribological system was assembled, one when the liquids and the pairs were put inside of a stainless steel vessel and others inside of a PTFE. Every tribological test was performed under 10N normal Ioad120mms ~(-1) of sliding speed. The friction coefficients were evaluated during 1000 cycles.