САМООРГАНИЗУЮЩИЕСЯ КОМПОЗИТНЫЕ ПОЛИМЕР-НАНОАЛМАЗНЫЕ ПОКРЫТИЯ ВАКУУМНЫХ КАТОДОВ

摘要

For the first time, the principles of the formation of thin-film nanocomposites detonation nanodiamonds-polymer, promising materials for highly cost-effective field-electron vacuum cathodes, are investigated. Coatings are deposited to oriented substrates (Ni, Si) during self-assembly from an evaporative aqueous solution based on the spin-coating technology. Field electron emission studies have demonstrated that the magnitude of the observed threshold voltage exceeds by more than ten times typical values for nanocarbon structures. At the same time, it is about ten times smaller than work function of bulk samples of diamond or graphite. The improvement of emission properties of the coating with polymers has been established in comparison with the deposition of films from a solution of diamond crystallites without a polymer.%Впервые исследованы процессы формирования тонкопленочных нанокомпозитов детонационный наноалмаз-полимер, перспективных материалов для высокоэкономичных автоэлектронных вакуумных катодов. Покрытия наносили на ориентированные подложки (Ni, Si) в процессах самосборки в испаряющемся водном растворе на основе технологии центрифугирования. Исследования полевой электронной эмиссии показали, что величина порогового напряжения превышает типичные значения для наноуглеродных структур более чем в десять раз. В то же время она примерно в десять раз меньше работы выхода из макроскопического алмаза или графита. Установлено улучшение стабильности эмиссионных свойств покрытия в присутствии полимеров по сравнению с нанесением пленок из раствора кристаллитов наноалмаза без полимеров.