The influence of aluminium deoxidation and sulphur content on oxide modification and machinability of steel

摘要

The influence of Al-deoxidation and various amounts of sulphur on Ca treated steel has been investigated. The effect of sulphur a aluminium on the modification of oxide inclusions has been reasoned by theoretical thermodynamic equilibrium analysis. The type inclusion formed depends on the aluminium and sulphur contents. For complete oxide shape control in which CaO-rich inclusions for the sulphur content must be relatively low for Al-killed steel. The oxide inclusion type of the experiments was in surprisingly go agreement with the prediction of thermodynamics. The influence of calcium and sulphur on the machinability and mechanical properti has also been demonstrated as well as the improvement of isotropy in steel obtained by Ca-addition.%Der Einfluss einer Aluminium desoxidation und des Schwefelgehaltes auf Ca-Iegierten Stahl wurde untersucht. Der Einfluss von Schwefel und Aluminium auf die Modifikation der Oxideinschlusse wurde mit theoretischen thermodynamischen Gleichgewichtsanalysen verdeutlicht. Die Art des gebilde-c ten Einschlusses hangt vom Aluminium- und Schwefelgehalt ab. Fur eine vollstandige Oxidformkontrolle sollte gewahrleistet sein, dass der Schwefelgehalt im Fall von AI-beruhigtem Stahl relativ niedrig sein sollte. Die Art des Oxideinschlusses, die in den Versuchen ermittelt wurde, stimmte uberraschend gut mit den thermodynamischen Vorausberechnungen uberein. Der Einfluss von Calcium und Schwefel auf die Zerspanbarkeit und die mechanischen Eigenschaften wird ebenso aufgezeigt, wie die Verbesserung der Isotropie bei Stahlen durch Zugabe von Calcium.