Porosity Development In Chars From Thermal Degradation Of Poly (p-phenylene Benzobisoxazole)

摘要

The main objective of this work was to investigate porosity development in carbonaceous materials formed by thermal degradation of the high thermal stability polymer, poly(p-phenylene benzobisoxazole) (PBO). Two varieties of PBO, as-spun (AS) and high-modulus (HM) were studied. Chars obtained at various polymer decomposition temperatures (selected on the basis of thermogravimetric and differential thermal analysis results) were characterized by elemental analysis, infrared spectroscopy, X-ray diffraction and CO2 adsorption at 273 K. The obtained adsorbents essentially contained narrow micro-pores, and maximum pore development took place at ca. 1000 K, when the polymer was not yet completely decomposed. At higher temperatures, there is a certain pore widening along with a displacement towards smaller pore sizes, and the pore volume significantly decreases.