Low-Temperature Processing of ZrB2-ZrC Composites by Reactive Hot Pressing

摘要

Dense ZrB2-ZrC and ZrB2-ZrC x～0.67 composites have been produced by reactive hot pressing (RHP) of stoichiometric and nonstoichiometric mixtures of Zr and B4C powders at 40 MPa and temperatures up to 1600 °C for 30 minutes. The role of Ni addition on reaction kinetics and densification of the composites has been studied. Composites of ～97 pct relative density (RD) have been produced with the stoichiometric mixture at 1600 °C, while the composite with ～99 pct RD has been obtained with excess Zr at 1200 °C, suggesting the formation of carbon deficient ZrC x that significantly aids densification by plastic flow and vacancy diffusion mechanism. Stoichiometric and nonstoichiometric composites have a hardness of ～20 GPa. The grain sizes of ZrB2 and ZrC x～0.67 are ～0.6 and 0.4 μm, respectively, which are finer than those reported in the literature.