Circumventing Practical Difficulties in Determination of Threshold Stress Intensity for Stress Corrosion Cracking of Narrow Regions of Welded Structures

摘要

Determination of the threshold stress intensity for stress corrosion cracking (K Iscc) of narrow areas such as weld and heat-affected zone (HAZ) of a weldment is a nontrivial task because of the requirements of large specimens in testing by the traditional techniques and the difficulty of restricting crack propagation to narrow regions in such specimens. This article describes a successful application of the circumferential notch tensile (CNT) technique to determine the K Iscc of narrow regions of the weld and HAZ. Also, the microstructure of the HAZ of the manual metal arc-welded steel was simulated over a relatively small length of specimens and its K Iscc in a hot caustic solution was determined successfully. Intergranular stress corrosion cracking was confirmed with a scanning electron microscope.