首页> 外文期刊>Metallurgical and Materials Transactions A >Influence of Mg on Solidification of Hypereutectic Cast Iron: X-ray Radiography Study
【24h】

Influence of Mg on Solidification of Hypereutectic Cast Iron: X-ray Radiography Study

机译:镁对过共晶铸铁凝固的影响:X射线射线照相研究

获取原文
获取原文并翻译 | 示例
           

摘要

Radiography using a synchrotron radiation X-ray source was performed to examine solidification and melting behaviors in hypereutectic cast iron specimens containing 0.002 and 0.05mass pctMg. The solidification sequence in the alloy containing 0.002mass pctMg was (1) nucleation and growth of graphite particles of which transformed to a flake-like shape, (2) growth of γ-Fe dendrites, (3) nucleation of graphite particles ahead of the interface just prior to the eutectic solidification, and (4) the eutectic solidification. In contrast, (1) and (2) occurred nearly at the same time in the specimen containing 0.05 mass pct Mg. The addition of 0.05mass pctMg significantly reduced the temperature range in which the graphite particles grew as the primary phase. Image-based analysis of melting behavior showed that even 0.05 mass pct addition was sufficient to modify the phase equilibrium of the liquid, γ-Fe, and graphite phases. Thus, the observed influence of Mg on the solidification sequence was attributed to the modification of the phase equilibrium. The influence was consistently explained by considering the shift of the eutectic composition to the carbon side in the pseudo-ternary system. It was also suggested that supersaturation of carbon in the melt increased as the temperature decreased even though the primary graphite particles existed. The supersaturation may cause the nucleation of the graphite particles just before the eutectic solidification.
机译:使用同步辐射X射线源进行射线照相,以检查含有0.002和0.05质量pctMg的过共晶铸铁样品的凝固和熔化行为。含有0.002质量pctMg的合金的凝固顺序为(1)石墨颗粒成核并生长为片状形状;(2)γ-Fe树枝状晶体的生长;(3)石墨颗粒在石墨之前的成核过程。界面在共晶凝固之前,以及(4)共晶凝固。相反,(1)和(2)在含有0.05质量%镁的样品中几乎同时发生。添加0.05质量pctMg显着降低了石墨颗粒作为主要相生长的温度范围。基于图像的熔融行为分析表明,即使添加0.05质量分也足以改变液相,γ-Fe和石墨相的相平衡。因此,观察到的镁对凝固顺序的影响归因于相平衡的改变。通过考虑准三元体系中低共熔成分向碳侧的移动来一致地解释这种影响。也有人提出,即使存在初级石墨颗粒,熔体中碳的过饱和度也会随着温度的降低而增加。过饱和可能会在共晶凝固之前引起石墨颗粒的形核。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱:kefu@zhangqiaokeyan.com

京公网安备:11010802029741号 ICP备案号:京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有
  • 客服微信

  • 服务号