Friction stir welding characteristics of different heat-treated-state 2219 aluminum alloy plates

摘要

Friction stir welding (FSW) of 2219-O and 2219-T6 aluminum alloys was performed to investigate the effects of the base material conditions on the FSW characteristics. The experimental results indicated that the base material condition has a significant effect on weld morphologies, weld defects, and mechanical properties of joints. In the 2219-O welds, no discernible interface exists between the stir zone (SZ) and the thermal-mechamcally affected zone (TMAZ), and weld defects are liable to form in the lower part of the weld. In the 2219-T6 welds, there is visible interface between the SZ and the TMAZ, and a weld nugget with an "onion ring"-like morphology clearly exists. The defects are liable to form in the upper part of the weld. The strength efficiency of 2219-O joints is 100%, while that of 2219-T6 joints is only up to 82%. In addition, the two types of joints have different fracture location characteristics.