In-situ investigation of stress-induced martensitic transformation in Ti-Nb binary alloys with low Young's modulus

摘要

Microstructure evolution, mechanical behaviors of cold rolled Ti-Nb alloys with different Nb contents subjected to different heat treatments were investigated. Optical microstructure and phase compositions of Ti-Nb alloys were characterized using optical microscopy and X-ray diffractometre, while mechanical behaviors of Ti-Nb alloys were examined by using tension tests. Stress-induced martensitic transformation in a Ti-30 at%Nb binary alloy was in-situ explored by synchrotron-based high-energy X-ray diffraction (HE-XRD). The results obtained suggested that mechanical behavior of Ti-Nb alloys, especially Young's modulus was directly dependent on chemical compositions and heat treatment process. According to the results of HE-XRD, α″-V1 martensite generated prior to the formation of α"-V2 during loading and a partial reversible transformation from α-V1 to β phase was detected while α"-V2 tran-formed to β completely during unloading.