Texture Development in Dual Phase α/β-Brass - Part Ⅱ: Recrystallization Textures

摘要

The development of the crystallographic texture in two phase α/β-brass Cu-40 % Zn containing 20 vol.% β phase was investigated separately for both phases by means of 3-dimensional orientation distribution functions (ODFs). The results were compared to those of the single phase alloy Cu-37% Zn and to literature data of Cu-30% Zn. Whereas the development of the rolling textures was subject to the first part of the current work, the present second part describes that of the recrystallization textures. Besides X-ray macrotexture analysis local orientation determinations in a SEM were performed. In the recrystallization behaviour of the fcc α phase larger differences between Cu-40 % Zn and homogeneous α-brass were observed, which could be attributed to a different nucleation behaviour in the vicinity of the bcc β grains. In the β phase mainly extensive recovery reactions occurred during recrystallization annealing.%In zweiphasigem α/β-Messing Cu-40 % Zn mit einem Anteil von 20 Vol.-% β-Phase wurde die Entwicklung der kristallographischen Textur beider Phasen mit Hilfe der 3-dimensionalen Orientierungsverteilungsfunktionen (OVFs) verfolgt. Die Ergebnisse wurden mit denen der einphasigen Legierung Cu-37 % Zn sowie mit Literaturdaten an Cu-30% Zn verglichen. Während die Entwicklung der Walztexturen Thema des ersten Teil dieser Arbeit war, behandelt der vorliegende zweite Teil die Rekristallisationstexturentwicklung. Neben Röntgentex-turmessungen wurden auch lokale Orientierungsbestimmungen im REM durchgeführt. Im Rekristallisationsverhalten der kfz α-Phase zeigten sich größere Unter-schiede zwischen Cu-40 % Zn und homogenem α-Messing, die auf ein unterschiedliches Keimbildungsverhalten in der Nähe der krz β-Körner zurückgeführt werden konnten. In der β-Phase liefen während der Rekristallisationsglühung hauptsächlich ausgeprägte Erholungsvorgänge ab.