Application of the Stoner-Wohlfarth model with interaction for the determination of the saturation magnetisation, anisotropy field,and mean field interaction in bulk amorphous ferromagnets

摘要

Magnetic hysteresis curves of bulk amorphous ferromagnet alloys of composition Nd_(60)Fe_(30)Al_(10), Nd_(60)Fe_(30)Al_(10) and Pr_(58)Fe_(24)Al_(18) have been measured in applied magnetic fields up to 9 T at temperatures in the range 10-350 K. The behaviour of the demagnetisation curve in the first quadrant is interpreted using a mean field interaction model as proposed by Callen et al. [Phys. Rev. B 16 (1977) 263], which extends the Stoner-Wohlfarth model [Philos. Trans. Roy. Soc. A 240 (1948) 599) for a random distribution of non-interacting uniaxial grains. Application of the mean field interaction model enables the determination of the saturation magnetisation M_s, anisotropy field H_a, and interaction parameter d, and from these other magnetic parameters, such as the anisotropy constant, K, are deduced. For the three alloys, the temperature dependent behaviour of M_s, H_a, d and K over the range 20-350 K are found to be qualitatively similar, though there are quantitative differences. In all cases M_s increases with decreasing temperature, both H_a and K increase with decreasing temperature, reaching a peak in the range 75-120 K, and then decreasing, and d decreases approximately linearly as the temperature decreases. The physical mechanisms responsible for coercivity in these materials are discussed in the context of random anisotropy and a strong pinning model of domain walls.