Properties of Diamine Chain Extended Polyurethane Urea Coatings

摘要

An effort has been made to understand the structure property correlation with different chain extender structure. For these, different moisture cured polyurethanes were synthesized and partially chain extended with various aromatic diamines. The remaining excess isocyanates in the polyurethane matrix were reacted with atmospheric moisture. Viscoelastic properties of these cured films were determined by Dynamic Mechanical Thermal Analyzer (DMTA). The mechanical properties such as tensile strength, adhesion strength and hardness were related to chemical composition and cohesion of the hard segment. Angle resolved X-ray Photoelectron Spectroscopy (AR-XPS) was used to determine the surface properties. The combined analysis indicates the degree of phase separation is the cause for the overall macroscopic properties and is dependent on the chain extender structure.%本研究では、異なる鎖伸長剤構造とその構造特性との関係を理解することを目的とした。この目的のため、異なる湿気硬化形ポリウレタンが合成され種々の芳香族ジアミンにより部分的に鎖伸長が行われた。ポリウレタンマトリックス中の過剰未反応イソシアネートは大気中の水と反応した。これらの硬化塗膜の動的粘弾性をDMTAにより測定した。引張強度、接着強度、硬度などの機械的性質はその化学組成と剛直セグメントに依存した。角度可変型X線光電子分光分析により塗膜表面の性状をしらべた。これらの結果から、相分離の程度は塗膜全体の巨視的性状を決定し、また鎖伸長剤構造に依存することが示唆された。