Exploring the use of rachis of chicken feathers for hydrogen storage

摘要

This research shows up the results obtained using samples of activated carbon synthesized from rachis of chicken feathers. The samples were characterized through nitrogen adsorption isotherms at -196 ℃, FTIR, SEM and XPS. The samples have a BET area between 88 and 314 m~2 g~(-1), showing a microporous and mesoporous structure. The results showed that the hydrogen storage was higher (3.5 wt/wt) in the sample obtained at the highest temperature (CFAC-450).