Effect of a large population of seeded alumina inclusions on crack initiation and small crack fatigue crack growth in Udimet 720 nickel-base disk superalloy

摘要

Crack initiation, crack coalescence and small crack growth behavior were monitored for over 400 seeded inclusions during interrupted low cycle fatigue testing conducted on the P/M Udimet 720 nickel disk alloy at 650 °C. Two types of seeded alumina inclusions with average sizes of 54 μm and 122 μm were used in the study performed at varying loading conditions resulting in LCF lives ranging from 2,000 cycles to over 1,000,000 cycles. The fatigue behavior was sub-categorized into four groups. Visual maps detailing inclusion size/cycle history were developed. The effect of surface residual stresses on the fatigue life was also investigated.