Tapered Main Poleヘッドのポールイレーズ解析

摘要

For a perpendicular writer, it is necessary to reduce the pole tip remanence as well as to improve the writing efficiency. To improve the writing efficiency for a narrow core width design, a tapered main pole geometry is proposed. We simulated the head remanence of the tapered main pole head with a micromagnetic model. To reduce the head pole tip remanence, a single magnetic domain structure forming a vortex state from the pole tip (ABS) to the tapered region is preferred. A tapered main pole structure with the trailing gap depth (TGD) below 30 run and the tapered angle (TG9) equal to about 30 degrees effectively improved the writing efficiency. This is achieved with a higher head field value of more than 1.3 times of the conventional structure. Moreover, the pole tip remanence is reduced to a value closer to the conventional structure.%高記録密度化に伴う狭コア幅記録ヘッドにおいて，コア幅の縮小とともに記録磁界の低下とポールイレーズの原因となる残留磁界の増大が懸念される．記録磁界を増加できる構造として提案されたTapered Main Pole へッドにおいて，残留磁界とヘッド構造との関係をマイクロマグネテイクスシミュレーションにより検討した．残留磁界の抑制には，テーパー部を含む主磁極の先端部で還流磁区を形成することが効果的である．テーパー部の開始位置を媒体対向面から30nm以下，テーパー部の角度を30°付近に低減した構造では，ポールの上面で独立した磁区が消失し還流磁区を形成する．この構造により，記録性能の向上（記録磁界1．3倍以上）と従来ヘッドと同等レベルの残留磁化特性を両立することが可能である．