Synthesis of Nano-Sized Spherical Barium-Strontium Ferrite Particles

摘要

Magnetic recording media requires good particle dispersion, a smooth surface, and small interparticle interaction to make an adequate signal-to-noise ratio (SNR). Well dispersed 50-60 nm sized spherical barium-strontium ferrite (S-Ba/Sr-Fe) nanoparticles were successfully prepared with 40 nm sized hematite precursor particles and BaCO_(3)/SrCO_(3) colloid. The coercivity and saturation magnetizations of S-Ba/Sr-Fe nano-particles were 1568 Oe and 48.6 emu/g, respectively. In order to evaluate magnetic interaction, magnetic tape was prepared using an Eiger mill with binder and organic solvent. (DELTA)M measurement showed the S-Ba/Sr-Fe nanoparticles in the tape had negative magnetic particle-to-particle interaction.