Research into Isolation of Cellulose Micro- and Nanofibres from Hemp Straw Using Cellulolytic Complex from Aspergillus niger

摘要

Cellulose micro- and nanofibers were produced on a base of pulp obtained as a result of thermal-mechanical and chemical pretreatment of hemp straw. Isolation of micro-and nanofibres was carried out using the enzymatic treatment with the use of a cellulolytic complex of Aspergillus niger and two-stage enzymatic and mechanical treatment. Nanofi-bres obtained by intense enzymatic treatment were characterized by a diameter of less than 100 nm. As a result of the two-stage enzymatic-mechanical treatment micro-and nanofibres were obtained with a diameter in the range of 25-400 nm and a length of several hundred nanometers to several micrometers.%Mikro- i nanow?ókna celulozowe zosta?y wytworzone na bazie masy celulozowej otrzymanej w wyniku wst?pnej obróbki termo-mechanicznej i chemicznej s?omy konopnej. Izolacja mikro- i nanow?ókien by?a przeprowadzona przy wykorzystaniu obróbki enzymatycznej z zastosowaniem kompleksu celulolitycznego z Aspergillus niger oraz obróbki dwuetapowej - enzymatycznej i mechanicznej dezintegracji. Nanow?ókna otrzymane w wyniku intensywnej obróbki enzymatycznej przypomina?y wygl?dem nanokrysztaly celulozowe wytwarzane na drodze hydrolizy kwasowej i charakteryzowa?y si? ?rednic? poni?ej 100 nm. W wyniku dwuetapowej obróbki enzymatyczno-mechanicznej otrzymano mikro- i nanow?ókna o ?rednicach w zakresie 25 - 400 nm i d?ugo?ci od kilkuset nanometrów do kilku mikrometrów. Dla porównania wyj?ciow? mas? celulozow? poddano jedynie obróbce mechanicznej, jednak nie doprowadzi?a ona do powstania nanow?ókien a jedynie do cz??ciowej fibrylizacji w?ókien celulozowych.