Fluoride Salt Dissociation in NaCl-KCl Salt Flux and its Effect on the Coalescence of Aluminium

摘要

Effects of fluoride additive concentration, temperature, aluminium alloy type on the coalescence of aluminium in salt flux melt were studied for the standard European salt flux for aluminium remelting, based on 70 wt-percent NaCl and 30 wt-percent KCl. The promoting power of fluoride increased as CaF_2< Na_3AlF_6< NaF< LiF. CaF_2 addition resulted in a maximum of coalescence rate at 1 to 2 percent CaF_2. Increase of temperature accelerated the coalescence. "Free" fluoride ion is discussed as an active component of the salt flux. The thermodynamics of the oxide film stripping was reviewed.%Die Einflusse der Konzentration, Temperatur, Art der Aluminiumlegierung auf die Koaleszenz des Aluminiums im Standardschmelzsalz (70 Masse-percent NaCl und 30 Masse-percent KCl) wurden untersucht. Die Fahigkeit des Fluo-ridsalzes, die Koaleszenz zu befordern, steigt in der Reihe CaF_2< Na_3AlF_6< NaF< LiF von links nach rechts an. Zugabe von CaF, ergab ein Maximum der Koaleszenzgeschwin-digkeit bei 1 bis 2 percent CaF, Bei hoheren Temperaturen stieg die Koaleszenzgeschwindigkeit an. "Freie" Fluoridionen wurden als die aktive Komponente des Schmelzsalzes betrachtet. Der Artikel gibt eine kritische Ubersicht auf die Thermodynamik der Oxidschichtablosung.