Effect of surface treatment of CAD/CAM resin composites on the shear bond strength of self-adhesive resin cement

摘要

This study examined the effects of sandblasting, hydrofluoric acid etching and priming on the shear bond strength of self-adhesive resin cement between seven different CAD/CAM resin composites and a resin composite core material at 24-h after cement mixing. Five surface treatments [control (C), sandblasting (S), priming (P), sandblasting with priming (SP), and 9% HF etching with priming (HFP)] were performed respectively for disc specimens of CAD/CAM blocks. There were no significant differences in bond strength among the C, S, and P, except for one block (p >0.05). SP showed a greater bond strength than S. Weibull moduli were not changed significantly among all treatments for all blocks, whereas the strengths with 5% and 95% failure probability of SP and HFP showed greater values than the others. The bond strengths of HFP were comparable to those of SP. Priming after sandblasting or HF etching could be effective to increase the bond strength of CAD/CAM blocks.