Green approach to corrosion inhibition of stainless steel in phosphoric acid of Artemesia herba albamedium using plant extract

摘要

Essential oil from aerial parts ofArtemisia herba-albafrom Morocco was hydrodistilled and its chemical composition oil was investigated by capillary GC and GC/MS. The major components were 1,8-cineole (35.6%) and camphor (24.1%).Artemisia herba-albaessential oil AHAO was tested as corrosion inhibitor of stainless steel (SS) in 1M H3PO4using potentiodynamic polarization (PDP) and electrochemical impedance spectroscopy measurements (EIS) and scanning electronically microscopy (SEM) studies. The results obtained showed that the essential oil of Artemisia reduces the corrosion rate. Tafel polarization method indicates that the plant extract behaves as a mixed type inhibitor. The inhibition efficiency increased with inhibitor concentration to attain 88% at 1g.L?1of oil at 298K. Nyquist diagrams obtained from impedance studies provide results confirming the anti-corrosion effect of the studied plant. The temperature effect on the corrosion behavior of (SS) in 1M H3PO4without and with AHAO at 1g.L?1was studied in the temperature range from 298 to 353K. Thermodynamic parameters suggested that the adsorption is spontaneous and exothermic process and support physical adsorption mechanism. The experimental data fits well into the Langmuir adsorption isotherm model. SEM/EDS studies provide the confirmatory evidence for the protection of (SS) by the green inhibitor. The results obtained from these methods used are in good agreement.