V2O5/Mn3O4/Nb2O5 codoped zinc oxide varistor ceramics were sintered at a temperature range as low as 875~950°C. The voltage clamping characteristics of V2O5/Mn3O4/Nb2O5 codoped zinc oxide varistor ceramics were investigated at a pulse current range of 1~50 A. The sintering temperature had a significant effect on clamp voltage ratio, which exhibits surge protection capabilities. The varistor ceramics sintered at 875°C exhibited the best clamping characteristics, in which the clamp voltage ratio was 2.69 at a pulse current of 50 A. The varistor ceramics sintered at 900°C exhibited the highest electrical stability, where = 3,824 V/cm (initial 3,909 V/cm), and E1 mA/cm2 = 27 (initial 39) after application of a pulse current of 100 A.
展开▼
机译:V 2 sub> O 5 sub> / mn 3 sub> O 4 sub> / nb 2 sub> O 5 sub>编排的氧化锌压敏电阻陶瓷在低至875〜950℃的温度范围内烧结。 V 2 sub> O 5 sub> / mn 3 sub> o 4 sub> / nb 2 在1〜50a的脉冲电流范围内研究了亚℃> O 5 sub>编码氧化锌压敏电阻陶瓷。烧结温度对钳位电压比具有显着影响,这表现出浪涌保护能力。在875°C时烧结的压敏电阻陶瓷表现出最佳夹紧特性,其中钳位电压比在50A的脉冲电流下为2.69。在900°C时烧结的压敏电阻陶瓷表现出最高的电稳定性,其中= 3,824 V / cm (初始3,909 v / cm),e 1 mA / cm 2 sup> sub> = 27(初始39)施加100a的脉冲电流后。
展开▼