Trilayer Films of YBa2Cu3O7?x/LaAlO3/YBa2Cu3O7?x with Superconducting Properties Prepared via Sol-Gel Method

摘要

The YBa2Cu3O7?x/LaAlO3/YBa2Cu3O7?x (YBCO/LAO/YBCO) heterogeneous trilayer film structures were prepared on the LaAlO3 (001) single-crystal substrate via the sol-gel method. The characteristics of the phase, orientation, and superconducting properties were studied via an X-ray diffractometer and a comprehensive physical property measurement system. The results show that when the LAO layer was thin (40 nm), the trilayer films were relatively pure and had a high c-axis orientation. When the nominal thickness of the LAO layer increased to 70 nm, non-c-axis oriented grains started to appear in the trilayer film. In this case, the top and bottom YBCO layers exhibited superconducting properties, and the resistance was found to be zero at 80.1 and 72.5 K, respectively. In addition, for the YBCO/LAO (40 nm)/YBCO structure, the intermediate LAO layer was too thin to completely cover the surface of the underlying YBCO. This resulted in point contact and micro-bridge contact in several micro-regions, thus forming a weak connection and exhibiting a current-voltage (I–V) characteristic similar to the direct-current (DC) Josephson effect. On the other hand, for the YBCO/LAO (70 nm)/YBCO structure, the thicker LAO layer could completely cover the underlying YBCO surface, which could isolate the superconducting current between the YBCO layers.