pure plant oil, biofuel, coconut oil, palm oil, jatropha oilSocket is the most important component in a prosthesis making. Performance criteria for prosthetic socket material include strength, durability, minimal weight, comfort, and minimal fabrication cost. This research attempts to analyze the strength of ramie fiber reinforced epoxy laminate composite as an alternative of socket prosthesis. The research based on ASTM D 3039/D 3039M for tensile strength and ASTM D 695 for compressive strength. The ramie fiber used was a continuous fiber 100 % Ne14'S, with Epoxy Resin Bakelite EPR 174 and Epoxy Hardener V-140. The sample test was created using a hand lay-up method. The result of this research is presented in a correlation of finsile strength (st), compression strength (sc), elasticity modulus (E) versus fraction volume of fiber (Vf). The result is then being compared with some of the prosthesis material’s strength produced by Otto Bock. The analysis was completed with the mode of the failure observation by using Scanning Electron Microscope (SEM). The result concludes that the ramie fiber reinforced epoxy laminate composite is potentially developed further as a socket prosthesis material on Vf 40 – 50 %. Tensile strength and specific strength that has been generated was higher than that of several materias for socket prosthesis, including fiberglass. The mode of the failure found were a brittle failure on Vf: 10-30%, debonding and delamination on Vf: 40-50%. Abstract in Bahasa Indonesia: Socket merupakan bagian terpenting dalam pembuatan prosthesis. Kriteria bahan socket prosthesis antara lain kekuatan, ketahanan, ringan, kenyamanan dan biaya produksi yang rendah. Penelitian ini bertujuan menganalisis kekuatan komposit laminate berpenguat serat rami epoksi sebagai bahan alternatif socket prosthesis. Pengujian kekuatan mengacu standar ASTM D 3039/D 3039M uji tarik dan ASTM D 695 uji tekan. Serat rami yang digunakan berupa serat kontinyu jenis ramie 100 % Ne.14’S dengan matriks Epoxy Resin Bakelite EPR 174 dan Epoxy Hardener V-140. Sampel uji dibuat dengan metode hand lay-up. Hasil pengujian ditampilkan dalam berbentuk hubungan kekuatan tarik (?t), tekan (?c), modulus elastisitas (E) versus fraksi volume serat (Vf). Hasil pengujian akan dibandingkan dengan kekuatan beberapa bahan prosthesis yang diproduksi oleh Otto Bock. Modus kegagalan diamati dengan bantuan Scanning Electron Microscope (SEM). Berdasarkan pengujian yang telah dilakukan dapat disimpulkan bahwa komposit berpenguat rami epoksi berpotensi untuk dikembangkan sebagai bahan socket prosthesis pada Vf 40–50%. Kekuatan tarik dan spesific strength yang dihasilkan lebih tinggi dari beberapa bahan prosthesis termasuk fiberglass. Modus kegagalan yang terjadi adalah brittle failure (getas) pada Vf : 10-30%, debonding (ikatan lepas) dan delaminasi pada Vf : 40-50%. Kata kunci: Komposit laminate rami epoksi, kekuatan bahan komposit, socket prosthesis.
展开▼
机译：纯植物油，生物燃料，椰子油，棕榈油，麻风树籽油是假体制造中最重要的成分。假牙插座材料的性能标准包括强度，耐用性，最小重量，舒适度和最小制造成本。本研究试图分析of麻纤维增强环氧层压板复合材料作为承窝假体的强度。该研究基于ASTM D 3039 / D 3039M的抗拉强度和ASTM D 695的抗压强度。所使用的麻纤维是100％Ne14'S连续纤维，具有环氧树脂胶木EPR 174和环氧树脂硬化剂V-140。样品测试是使用手工铺网方法创建的。这项研究的结果以纤维的易碎强度（st），抗压强度（sc），弹性模量（E）与纤维体积分数（Vf）的关系表示。然后将结果与奥托·博克（Otto Bock）生产的某些假体材料的强度进行比较。通过使用扫描电子显微镜（SEM）以故障观察的模式完成分析。结果得出结论，the麻纤维增强环氧层压板复合材料有可能作为Vf 40 – 50％的承窝假体材料进一步开发。所产生的拉伸强度和比强度高于包括玻璃纤维在内的几种用于套接字假体的材料的拉伸强度和比强度。发现的破坏模式是在Vf上为脆性破坏：10-30％，在Vf上发生脱粘和分层：40-50％。印度尼西亚语中的摘要：插座穆鲁帕坎·巴吉安（pentian）缠绕达兰（pelam）假肢。 Kriteria bahan套筒假体antara lain kekuatan，ketahanan，ringan，kenyamanan dan biaya produksi yang rendah。 Penelitian ini bertujuan menganalisis kekuatan komposit层压板berpenguat serat rami epoksi sebagai bahan交替套假体。 Pengjianan kekuatan mengacu标准ASTM D 3039 / D 3039M uji tarik dan ASTM D 695 uji tekan。 Serat rami yang digunakan berupa serat kontinyu jenis ramie 100％Ne.14's dengan matriks环氧树脂胶木EPR 174 dan环氧树脂硬化剂V-140。 Sampel uji dibuat dengan metode上篮。 Hasil pengujian ditampilkan dalam berbentuk hubungan kekuatan tarik（？t），tekan（？c），弹性模量（E）相对于fraksi量浆液（Vf）。 Hasil pengujian akan dibandingkan dengan kekuatan beberapa bahan假肢yang diproduksi oleh Otto Bock。 Modus kegagalan diamati dengan bantuan扫描电子显微镜（SEM）。 Berdasarkan pengujian yang telah dilakukan dapat disimpulkan bahwa komposit berpenguat rami epoksi berpotensi untuk dikembangkan sebagai bahan假体pada Vf 40–50％。 Kekuatan tarik dan spesific strength阳dihasilkan lebih tinggi dari beberapa bahan假体termasuk玻璃纤维。 Modus kegagalan yang terjadi adalah脆性破坏（getas）pada Vf：10-30％，脱胶（ikatan lepas）和de delaminasi pada Vf：40-50％。 Kata kunci：Komposit层压板rami epoksi，kekuatan bahan komposit，假牙。
展开▼
