Evaluation of Degradation in Nanofilled Adhesive Resins Using Quantitative Light-Induced Fluorescence

摘要

The aim of this study was to evaluate degradation in commercial dental nanofilled adhesive resins using quantitative light-induced fluorescence (QLF). Three adhesives were selected: D/E resin (DR), Single Bond Plus (SB), and G-Bond (GB). The adhesives were mixed with porphyrin for the QLF analysis. Specimens were prepared by dispensing blended adhesives into a flexible mold and polymerizing. Then, the QLF analysis of the specimens was done and the porphyrin values (Simple Plaque Score andΔR) were measured. After thermocycling of the specimens (5000 cycles, 5 to 55°C) for the degradation, the specimens were assayed by QLF again. The porphyrin values were analyzed using pairedt-test at a 95% confidence level. A significant reduction in SPS was observed in all groups after thermocycling. TheΔRsignificantly decreased after thermocycling except areaΔR30 of SB group. Overall, porphyrin values decreased after thermocycling which indicates that the degradation of the adhesive resins may be measured by the change of porphyrin value. The QLF method could be used to evaluate the degradation of adhesive resin.