Kinetics of conversion of brushite coatings to hydroxyapatite in alkaline solution

摘要

This work describes the kinetics of conversion of brushite coatings, produced by chemical deposition, to hydroxyapatite. The conversion was performed in alkaline solution at three temperatures: 50°C, 55°C, and 60°C. The evolution of the transformation was assessed by X-ray diffraction, and the phase fractions were determined by Rietveld refinement. The Johnson–Mehl–Avrami equation was applied to the data in order to describe the conversion mechanisms. The value of 42kJ/mol obtained for the conversion activation energy is of the same order as found in similar surface-controlled dissolution processes. The Avrami exponent wasn=3.5, which is consistent with an interface-controlled growth of three-dimensional HA crystals with decreasing nucleation rate.