Influence of composition and powder/water ratio on adhesion strength and initial viscosity of powder-type denture adhesives based on CMC-Na and PVM-MA

摘要

We evaluated the influence of the composition and powder/water (P/W) ratio of powder-type denture adhesives (DA) based on sodium carboxymethyl cellulose (CMC-Na) and poly(methyl vinyl ether-maleic anhydride) (PVM-MA) on the strength of adhesion to acrylic resin and initial viscosity. Twenty types of DA were prepared by mixing CMC-Na and PVM-MA at various weight ratios with distilled water in P/W ratios ranging from 0.125 to 0.500. Adhesion strength and viscosity were measured using a universal testing machine and a controlled-stress rheometer, respectively. A higher percentage of CMC-Na and higher P/W ratios resulted in higher adhesion strength and viscosity. The effect of the CMC-Na/PVM-MA weight ratio on adhesion strength and viscosity was larger than that of the P/W ratio. DA with higher viscosity had higher adhesion strength. These results suggest that the adhesion strength and initial viscosity of powder-type DA can be controlled via the P/W ratio and the CMC-Na/PVM-MA weight ratio.