Influence of CaO Addition, FeO/SiO 2 , and MgO/SiO 2 on the Melting Characteristic Temperatures of FeO-SiO 2 -MgO-CaO System

摘要

In order to decrease the oxidation temperature of fayalite in molten nickel slags, the influence of CaO addition, FeO/SiO 2 , and MgO/SiO 2 on melting characteristic temperatures of FeO-SiO 2 -MgO-CaO system were investigated. The melting characteristic temperatures, including softening temperature ( T s ), hemispherical temperature ( T h ), and flow temperature ( T f ),were measured with hot stage microscope. Experimental results showed that the melting characteristic temperatures first decreased sharply and then increased slowly with increasing w (CaO) for samples at given FeO/SiO 2 and MgO/SiO 2 ratios. The melting characteristic temperatures of samples without CaO addition were much higher than that of samples with different CaO addition, which was mainly caused by the phase components at different compositions. The variation of melting characteristic temperatures were described in detail. Phase components and liquid fractions were calculated by FactSage 7.1, which was good agreement with the XRD patterns.