Polar Order Evolutions near the Rhombohedral to Pseudocubic and Tetragonal to Pseudocubic Phase Boundaries of the BiFeO₃-BaTiO₃ System

摘要

Solid solutions of (1-x)BiFeO₃-xBaTiO₃ (BF-BT, 0.05 ≤ x ≤ 0.98) were prepared and characterized. It was found that the dielectric constant ε_m, remnant polarization P_r and piezoelectric coefficient d₃₃ reach their maximum values near the rhombohedral–pseudocubic phase boundary. In particular, the 0.7BF-0.3BT composition shows large polarization (P_r 20 μC/cm2) and a temperature-stable piezoelectric property (d₃₃ 100 pC/N when the annealing temperature is lower than ~400 °C). Near the tetragonal–pseudocubic phase boundary, ε_m and P_r decrease, and the piezoelectric property vanishes when the BF content reaches 4 mol %.