Effect of Alternating Stray Current and Stress on the Corrosion Behavior of X80 Pipeline Steel in Soil Simulated Solution

摘要

The corrosion behavior of X80 pipeline steel in 3.5 wt.% NaCl solution and simulated Dagang soilsolution under different alternating current (AC) electrical densities was studied using the weight lossmethod, and was tested and analyzed using the electrochemical test technique and surface analysistechnique, such as open circuit potential (OCP), polarization curve and scanning electron microscopy(SEM). The results showed that the corrosion potential of X80 pipeline steel was negative under thecoupling of AC and stress. With the increase of AC stray current density, the negative shifted rate ofcorrosion potential increased, which indicated that the electrochemical corrosion behavior of X80pipeline steel aggravated due to the coupling of AC stray and stress. In addition, the coupling of ACstray current and stress affected the corrosion process of X80 pipeline steel, which did not show anytendency of passivation in the experimental. Under the action of the alternating stray current, thereduction reaction of H2 and O2 occurred in X80 pipeline steel in the solutions of 3.5% NaCl andDagang soil. When the applied stress was kept constant, the corrosion morphology of X80 pipelinesteel samples underwent uniform corrosion under low AC stray current density (0 - 100 A/m2),whereas the corrosion morphology of X80 pipeline steel samples showed that the pitting corrosionoccurred under the action of high AC stray current density (100 - 300 A/m2).