Characterisation and understanding of the corrosion behaviour of the nugget in a 2050 aluminium alloy Friction Stir Welding joint

摘要

The corrosion behaviour of the nugget of a Friction Stir Welding joint employing a 2050 Al-Cu-Li alloy was investigated. The results showed that the nugget was susceptible to both intergranular and intra-granular corrosion. Such corrosion behaviour was related to microstructural heterogeneities observed on a microscopic scale. Furthermore, heterogeneities in the corrosion behaviour of the nugget observed on a macroscopic scale were evidenced by a different corrosion behaviour from the top to the bottom of the nugget and by a localisation of the corrosion damage related to the "Onion ring structure". Critical microstructural parameters were identified to explain the results.