机译:激光表面淬火镍 - 铝青铜合金的微观结构改性及改善耐腐蚀性
Tianjin Univ Sch Mat Sci & Engn Tianjin Key Lab Composite & Funct Mat Tianjin 300072 Peoples R China|Shanghai Jiao Tong Univ State Key Lab Met Matrix Composites Shanghai 200240 Peoples R China;
Tianjin Univ Sch Mat Sci & Engn Tianjin Key Lab Composite & Funct Mat Tianjin 300072 Peoples R China;
Tianjin Univ Sch Mat Sci & Engn Tianjin Key Lab Composite & Funct Mat Tianjin 300072 Peoples R China;
Tianjin Univ Sch Mat Sci & Engn Tianjin Key Lab Composite & Funct Mat Tianjin 300072 Peoples R China;
Shanghai Jiao Tong Univ State Key Lab Met Matrix Composites Shanghai 200240 Peoples R China;
Shandong Univ Sci & Technol Coll Mech & Elect Engn Qingdao 266590 Shandong Peoples R China;
Kunming Univ Sci & Technol Sch Mat Sci & Engn Kunming 650093 Yunnan Peoples R China;
Tianjin Univ Sch Mat Sci & Engn Tianjin Key Lab Composite & Funct Mat Tianjin 300072 Peoples R China;
Laser surface quenching; Nickel-aluminum bronze; Corrosion product film; Corrosion behavior;
机译:用铬离子注入表面改性提高镍铝青铜的耐腐蚀性
机译:改善镍铝青铜的耐腐蚀和气蚀性能的微结构设计
机译:通过喷丸处理改善镍 - 铝青铜(NAB)合金的耐腐蚀性能
机译:组合物与微观结构对镍铝青铜海水耐腐蚀的影响
机译:铝合金6013的激光表面熔化可改善应力腐蚀和抗腐蚀疲劳性。
机译:Ti含量对激光熔覆CoCrFeNiTix高熵合金显微组织和耐蚀性的影响
机译:通过控制Ni涂层的晶粒尺寸改善镍铝青铜(NAB)合金的机械性能和耐腐蚀性