Effect of metakaolin and foundry sand on the near surface characteristics of concrete

摘要

This paper deals with the effect of foundry sand (FS) and metakaolin (MK) on the near surface characteristics of concrete. A control concrete having cement content 450 kg/m3 and w/c of 0.45 was designed. Cement was replaced with three percentages (5%, 10%, and 15%) of metakaolin weight, and fine aggregates were replaced with 20% foundry sand. Tests were conducted for initial surface absorption, sorptivity, water absorption and compressive strength at the ages of 35, 56, and 84 days. Test results indicated that with the increase in MK content from 5% to 15%, there was a decrease in the initial surface absorption, decrease in the sorptivity till 10% metakaolin replacement. But at 15% MK replacement an increase in sorptivity was observed. All mixtures showed low water absorption characteristic i.e. less than 10%. Compressive strength shared an inverse relation with sorptivity. Higher MK replacements of 15% are not helpful in improving inner core durability, even though it helps in improving surface durability characteristics. Inclusion of foundry sand resulted in reduction in compressive strength. This aspect cements the findings that addition of FS causes permeability of concrete to increase causing in an increase in sorptivity and water absorption of concrete.