机译:用碳酸固化固化和进一步水固化的硬化水泥浆料组成和微观结构
Shenzhen Univ Sch Civil Engn Guangdong Prov Key Lab Durabil Marine Civil Engn Key Lab Durabil Civil Engn Shenzhen Shenzhen 518060 Peoples R China|Shenzhen Univ Coll Phys & Optoelect Engn Shenzhen 518060 Peoples R China|China Bldg Mat Acad State Key Lab Green Bldg Mat Beijing 100024 Peoples R China;
Shenzhen Univ Sch Civil Engn Guangdong Prov Key Lab Durabil Marine Civil Engn Key Lab Durabil Civil Engn Shenzhen Shenzhen 518060 Peoples R China;
Shenzhen Univ Sch Civil Engn Guangdong Prov Key Lab Durabil Marine Civil Engn Key Lab Durabil Civil Engn Shenzhen Shenzhen 518060 Peoples R China;
Tianjin Univ State Key Lab Hydraul Engn Simulat & Safety Tianjin 300072 Peoples R China;
Qingdao Univ Technol Dept Civil Engn Qingdao 266033 Peoples R China;
Shenzhen Univ Sch Civil Engn Guangdong Prov Key Lab Durabil Marine Civil Engn Key Lab Durabil Civil Engn Shenzhen Shenzhen 518060 Peoples R China;
Carbonation curing; Reaction products; Polymorphs of CaCO3; Calcium-silicate-hydrate; Microstructure;
机译:水泥浆料的微观结构受环境压力碳化固化
机译:碳酸固化制度对波特兰水泥浆料强度和微观结构的影响
机译:早期碳酸化固化作用对高初始强度波特兰水泥浆料的微观结构
机译:水下长期凝结后水胶比低的波特兰水泥浆的微观结构
机译:硅酸盐石灰石水泥的碳化碳化及透水混凝土性能
机译:高炉炉渣替代率和固化方法对水泥浆料碳化后孔结构变化的影响
机译:使用纳米压痕和29Si MAS NMR检查在高温和高压下固化的硬化水泥浆的微观结构组成
机译:固化条件对粉煤灰替代水泥浆体水分损失和水化的影响